Engine Bearings, Bimetal Bearings, Sintered Bushings, Bronze Bushings, Steel Bushings, Thrust Washers, Wear Plates, Bimetal Bearings, Polymer Bush, Metal Powders, Bimetal Strip, Pressure Sintering, Bearings, Bushings, Washers – R G Bronze Mfg Co Pvt Ltd, Chennai India.

Alloy Powder Manufacturing

Copper-based Alloy Powder at RGB is produced by Hydra Atomization process. Copper, Lead, Tin etc., in the form of virgin metals are melted down and disintegrated into fine droplets by means of a high velocity atomizing

medium. The metal droplets cool and solidify as they settle at the bottom of the atomization tank. The slurry is transferred to a dual cone drier for drying. The dried powder is sieved to get the required distribution of particles and blended to get a homogeneous mixture.

Water atomization

Gas atomization

Read More Close

Sintering

Cold rolled steel strips are cleansed thoroughly for sintering. The pre-mixed bearing alloy powder is spread over the continuously moving prepared steel strip which advances into a multi zone furnace under reduced atmosphere

The powder particles reach a semi molten stage to attain metallic bond. The strip is then compacted to increase the density and re-sintered to improve the bond strength and to achieve the final desired size. The Sintered Bimetal strip is slit to the required width for manufacture of Plain Shaft Bearings, Bushings and Thrust Washers.

Production Process – Sintered Copper Lead Alloy

Read More Close

Babbit Casting

Cold rolled steel strip is prepared thoroughly for casting. The bonding surface is tinned, before the Babbitt alloy is cast on the surface followed by water quenching, Milling and Knifing to achieve the final desired size

Production Process – Cast Lead/Tin base

Bimetal strips produced at RGB undergo strict laboratory evaluation such as visual, dimensional, physical/chemical and micro structure examination.

Steel Backing

Cold rolled steel strips used in the manufacture of Bearings, Bushings and Thrust Washers confirms to SAE 1008, SAE 1010 and SAE 1020 standards. Steel backing not only increases the mechanical strength but also holds to a minimum dimensional change caused by thermal expansion.

Read More Close

Diffusion Bonding Of Friction /Anti-Friction Products

Antifriction and Friction parts at RGB are also produced by Pressure Sintering Process. The premixed powder is compacted to the required shape in a rigid steel carbide die using high compacting pressure The resultant

green piece is pressure-sintered to a steel backing in a controlled atmosphere furnace thus achieving a metallurgical bond.

Pressure Sintering

Read More Close

Electroplating

Overlay plating in an engine bearing is made of thin plated surface layer (0.025 mm thick) of Lead-Tin-Copper over nickel. The Babbitt overlay provides embedability, long life and superior performance Copper

Lead Bearings and Bushings are plated with the above soft overlay in an excellent facility available in-house.